FLEXO FALT

FLEXO FALT is a high performance, ready to use, cold applied,single component and elastrometic high build liquid waterproofing membrance based on aliphatic, polurethane modifiedbitumen emustion

KRISHNA FLEXO FALT is a high performance, ready to use, cold applied,single component and elastrometic high build liquid waterproofing membrance based on aliphatic, polurethane modifiedbitumen emustion. FLEXO FALT forms a seamless,highly elastic and durable films that adheres well to most common substrates e.g concrete,cement blocks,wood,existing roof felts.FLEXO FALT is highly resistance   to a clorides and shlphetes commanly present in the soil.it is also highly UV resistant.


USES :

  • New roofs
  • Balconies, Terraces, Parking garages, Asbestos and concrete roofs.
  • Industrial washrooms & shower.
  • Water reservoirs and swimming pools.
  • Foundation, cellar walls, retaining walls, bridges abutments.
  • Refurbishing of old waterproofing system including torch - on membrane.
  • Facade damp proofing.
  • Water proofing / curing membrane and protective coating for sub structure.


TYPICAL PRODUCT CHARACTERISTICS :

AppereanceThixotropic black emulsion dries to a black flexible protective membrane.
Non-volatile content65 % min
Rubber Content on dry filmApprox. 15 %
Elongation (ASTM D 412)500 % Approximately
Ultimate tensile strength (ASTM D 412)2 N / mm2
Sp. Gr.1.2 + / - 0.01
pH>9
UV and Ozone stabilityExcellent
Chemical stabilityResists most common spills like oil and mild chemicals. Will not resists solvents which will dissolve bitumen.
Tempurature- 25º / + 120º C


PROPERTIES OF DRY FILM :

Softening point R & B (ASTM D36 - 84)> 120º C
water vapour permeability (ASTM E96 - 92)> 0.15 gr / m2 / day
Elongation at break (ASTM D 412)> 900 %
Recovery at 350 % elongation (ASTM D 412)> 50 %
Resistance to water (ASTM D 2939)No Blistering or re-emulsification
Protection of building against ground waterAs per BS 1102 Code of practice
Curing membrane ASTM C 309 : 1998


  1. Single component and cold applied.
  2. FLEXO FALT  has excellant UV resistance and long term ageing stability.
  3. Cured membrances from FLEXO FALT remain highly flexble event   at extreames of temprature(-25c  to 120 c).
  4. Excellant vapour barrier.
  5. Easy to use.
  6. Enviroment Friendly.
  7. Resistant to chlorides and sulphet commanly present in the soil.
  8. Compartible with cementatious tilling    adhesive.


SURFACE PREPARATION :

All surfaces should be sound, clean and free of contaminants. Absorbent surfaces e.g. concrete should preferably be dampened with water. In kitchens, toilets and other wet areas all the openings should be properly sealant. On all weak points such as cracks or around the pipes use a woven fibreglass mesh as reinforcement between the two coats FLEXO FAlT.






APPLICATION :

FLEXO FALT can be applied by brush, roller or sequeegee. Hot, dry or very porous substrate should be dampened with clean water proir to application of FLEXO FALT.  When two or more coats are required, ensure that the preceding coat is fully dry before applying the successive coat, which should be applied at right angle to proceeding coat. FLEXO FALT  also acts as a non-degradable curing membrane: hence it may applied immediately after the removel of mould, to the concrete structure, which has no aesthetic value such as the sub structure of the building.


APPLICATION RATE :

Primer1 part FLEXO FALT  + 1 part water
Base Coat1 part FLEXO FALT (Diluted with water upto 20 % max i.e. 4 Lts max per 20 kgs bucket of FLEXO FALT)
Top Coat1 part FLEXO FALT (Diluted with water upto 10 % max i.e. 2 Lts max per 20 kgs bucket fo FLEXO FALT)


COVERAGE :

Primer 250 grams / m2 / coat
Base coat0.5 kg / m2 / coat
Top coat0.5 kg / m2 coat

Layer Thickness : 15 mm

For highly performance glass Fibre reinforcement can be applied between 2 coats of FLEXO FALT.